Paryls Polyphenylsulfones (UJU-PPSU)

Properties

Properties Test Standard Test Condition S.I. Unit F1150 F1250 F1350
Density ISO 1183 -1
g/cm3 1.29 1.29 1.29
Melt Mass-flow Rate ISO 1133 365°C/5kg g/10min 15 25 35
Tensile Strength ISO 527 -1/-2 10mm/min MPa 76 76 75
Tensile Modulus ISO 527 -1/-2 10mm/min MPa 2335 2335 2335
Elongation at yield ISO 527 -1/-2 10min/mm % 7.5 7.5 7.5
Flexural Strength ISO 178 2mm/min MPa 108 108 108
Flexural Modulus ISO 178 2mm/min MPa 2480 2480 2480
Izod Notched Impact Strength ISO 180/1A 23°C kJ/m2 72 70 68
Tg ISO 11357 -3
°C 220 220 220
HDT ISO 75 -1/-2 1.80 MPa °C 206 206 206
Surface Resistivity IEC 60093
Ω 10^15 10^15 10^15
Molding Shrinkage ISO 294-4
% 0.7-1.0 0.7-1.0 0.7-1.0
Water Absorption ISO 62 23°C/24hr % 0.35 0.35 0.35
Flammability UL94 0.75 - 3.00mm Class V-0 V-0 V-0
GWFI IEC60695-2-12 0.75 - 3.00mm °C 960 960 960

Typical Processing Conditions for Paryls Polyphenylsulfones (UJU-PPSU)


Optimum Range
Melt Temp 365C 340-385C
Barrrel Zone Temp Rear 350C 340-360C
Center 365C 350-370C
Front 375C 365-385C
Mold Temp 190C 170-200C
Processing Temp (Upper Limit) 420C
Injection Speed Moderate to High
Pre-dry Requirements 150-180C, 4-6 hrs

Regulatory Approvals


Paryls Polysulfones (UJU-PSU)

Properties

Properties Test Standard Test Condition S.I. Unit F3050 F3150 F3250
Density ISO 1183 -1
g/cm3 1.24 1.24 1.24
Melt Mass-flow Rate ISO 1133 365°C/5kg g/10min 15 25 35
Tensile Strength ISO 527 -1/-2 10mm/min MPa 65 68 68
Tensile Modulus ISO 527 -1/-2 10mm/min MPa 2800 2800 2800
Elongation at yield ISO 527 -1/-2 10min/mm % 22 22 22
Flexural Strength ISO 178 2mm/min MPa 108 108 108
Flexural Modulus ISO 178 2mm/min MPa 2500 2500 2500
Izod Notched Impact Strength ISO 180/1A 23°C kJ/m2 6.0 6.0 6.0
Tg ISO 11357 -3
°C 185 185 185
HDT ISO 75 -1/-2 1.80 MPa °C 172 172 172
Surface Resistivity IEC 60093
Ω 10^15 10^15 10^15
Molding Shrinkage ISO 294-4
% 0.3-0.4 0.3-0.4 0.3-0.4
Water Absorption ISO 62 23°C/24hr % 0.3 0.3 0.3
Flammability UL94 0.75 - 3.00mm Class V-1 V-1 V-1

Typical Processing Conditions for Paryls Polysulfones (UJU-PSU)


OptimumRange
Melt Temp 270C 250-290C
Barrrel Zone TempRear 300C 280-310C
Center 310C 300-320C
Front 320C 310-340C
Mold Temp 130C 120-160C
Processing Temp (Upper Limit) 400C
Injection Speed Moderate to High
Pre-dry Requirements 150-180C, 4-6 hrs

Regulatory Approvals